JIS  SPECIFICATIONS

JIS-G-4051 (1979) CARBON STEELS FOR MACHINE STRUCTURAL USE
Symbol of class%C%Mn%S%P%Si%Cr%Ni%Mo%V%B%W%Al
S 10 C0.080/0.130.30/0.600.035 max0.030 max0.15/0.35-------
S 12 C0.10/0.150.30/0.600.035 max0.030 max0.15/0.35-------
S 15 C0.13/0.180.30/0.600.035 max0.030 max0.15/0.35-------
S 17 C0.15/0.200.30/0.600.035 max0.030 max0.15/0.35-------
S 20 C0.18/0.230.30/0.600.035 max0.030 max0.15/0.35-------
S 22 C0.20/0.250.30/0.600.035 max0.030 max0.15/0.35-------
S 25 C0.22/0.280.30/0.600.035 max0.030 max0.15/0.35-------
S 28 C0.25/0.310.60/0.900.035 max0.030 max0.15/0.35-------
S 30 C0.27/0.330.60/0.900.035 max0.030 max0.15/0.35-------
S 33 C0.30/0.360.60/0.900.035 max0.030 max0.15/0.35-------
S 35 C0.32/0.380.60/0.900.035 max0.030 max0.15/0.35-------
S 38 C0.35/0.410.60/0.900.035 max0.030 max0.15/0.35-------
S 40 C0.37/0.430.60/0.900.035 max0.030 max0.15/0.35-------
S 43 C0.40/0.460.60/0.900.035 max0.030 max0.15/0.35-------
S 45 C0.42/0.480.60/0.900.035 max0.030 max0.15/0.35-------
S 48 C0.45/0.510.60/0.900.035 max0.030 max0.15/0.35-------
S 50 C0.47/0.530.60/0.900.035 max0.030 max0.15/0.35-------
S 53 C0.50/0.560.60/0.900.035 max0.030 max0.15/0.35-------
S 55 C0.52/0.580.60/0.900.035 max0.030 max0.15/0.35-------
S 58 C0.55/0.610.60/0.900.035 max0.030 max0.15/0.35-------
S 09 CK0.070/0.120.30/0.600.025 max0.025 max0.15/0.35-------
S 15 CK0.13/0.180.30/0.600.025 max0.025 max0.15/0.35-------
S 20 CK0.18/0.230.30/0.600.025 max0.025 max0.15/0.35-------
Notes : As impurites Cu,Ni,Cr and Ni+Cr for classes S 09 CK,S 15 CK, S 20 CK shall not exceed respectively 0.25%,0.20%,0.20% and 0.30% and Cu, Ni,Cr and Ni +Cr for throughout other classes shall not exceed respectively 0.30%,0.20%, 0.20% and 0.35
JIS G 4052 (1979) STRUCTURAL STEELS WITH SPECIFIED HARDENABILITY BANDS
Symbol of classReference previous symbol%C%Mn%S%P%Si%Cr%Ni%Mo%V%B%W%Al
SMn420HSMn21H0.16/0.231.15/1.550.030 max0.030 max0.15/0.35-------
SMn433HSMn1H0.29/0.361.15/1.550.030 max0.030 max0.15/0.35-------
SMn438HSMn2H0.34/0.411.30/1.700.030 max0.030 max0.15/0.35-------
SMn443HSMn3H0.39/0.461.30/1.700.030 max0.030 max0.15/0.35-------
SMnC420HSMnC21H0.16/0.231.15/1.550.030 max0.030 max0.15/0.350.35/0.70------
SMnC443HSMnC3H0.39/0.461.30/1.700.030 max0.030 max0.15/0.350.35/0.70------
SCr415HScr21H0.12/0.180.55/0.900.030 max0.030 max0.15/0.350.85/1.25------
SCr420HScr22H0.17/0.230.55/0.900.030 max0.030 max0.15/0.350.85/1.25------
SCr430HScr2H0.27/0.340.55/0.900.030 max0.030 max0.15/0.350.85/1.25------
SCr435HScr3H0.32/0.390.55/0.900.030 max0.030 max0.15/0.350.85/1.25------
SCr440HScr4H0.37/0.440.55/0.900.030 max0.030 max0.15/0.350.85/1.25------
SCM415HSCM21H0.12/0.180.55/0.900.030 max0.030 max0.15/0.350.85/1.25-0.15/0.35----
SCM418H-0.15/0.210.55/0.900.030 max0.030 max0.15/0.350.85/1.25-0.15/0.35----
SCM420HSCM22H0.17/0.230.55/0.900.030 max0.030 max0.15/0.350.85/1.25-0.15/0.35----
SCM435HSCM3H0.32/0.390.55/0.900.030 max0.030 max0.15/0.350.85/1.25-0.15/0.35----
SCM440HSCM4H0.37/0.440.55/0.900.030 max0.030 max0.15/0.350.85/1.25-0.15/0.35----
SCM445HSCM5H0.42/0.490.55/0.900.030 max0.030 max0.15/0.350.85/1.25-0.15/0.35----
SCM822HSCM24H0.19/0.250.55/0.900.030 max0.030 max0.15/0.350.85/1.25-0.35/0.45----
SNC415HSNC21H0.11/0.180.30/0.700.030 max0.030 max0.15/0.350.20/0.551.95/2.50-----
SNC631HSNC2H0.26/0.350.30/0.700.030 max0.030 max0.15/0.350.55/1.052.45/3.00-----
SNC815HSNC22H0.11/0.180.30/0.700.030 max0.030 max0.15/0.350.65/1.052.95/3.50-----
SNCM220HSNCM21H0.17/0.230.60/0.950.030 max0.030 max0.15/0.350.35/0.650.35/0.750.15/0.30----
SNCM420HSNCM23H0.17/0.230.40/0.700.030 max0.030 max0.15/0.350.35/0.651.55/2.000.15/0.30----
Remarks :1. As impurities Cu shall not exceed 0.305 throughout all classes 2. As impurities Ni shall not exceed 0.25% excepting nickel chromium steel and nickel chromium molybdenum steel 3. Cr in manganese steel shall not exceed 0.35
JIS G 4102 (1979) NICKEL CHROMIUM STEELS
Symbol of classReference previous symbol%C%Mn%S%P%Si%Cr%Ni%Mo%V%B%W%Al
SNC 236SNC 10.32/0.400.50/0.800.030 max0.030 max0.15/0.350.50/0.901.00/1.50-----
SNC 415SNC 210.12/0.180.35/0.650.030 max0.030 max0.15/0.350.20/0.502.00/2.50-----
SNC 631SNC20.27/0.350.35/0.650.030 max0.030 max0.15/0.350.60/1.002.50/3.00-----
SNC 815SNC 220.12/0.180.35/0.650.030 max0.030 max0.15/0.350.70/1.003.00/3.50-----
SNC 836SNC 30.32/0.400.35/0.650.030 max0.030 max0.15/0.350.60/1.003.00/3.50-----
Remarks  1. As impurities Cu shall not exceed 0.30% throughout all classes
JIS G 4103 (1979) NICKEL CHROMIUM MOLYBDENUM STEELS
Symbol of classReference previous symbol%C%Mn%S%P%Si%Cr%Ni%Mo%V%B%W%Al
SNCM 220SNCM 210.17/0.230.60/0.900.030 max0.030 max0.15/0.350.40/0.650.40/0.700.15/0.30----
SNCM 240SNCM 60.38/0.430.70/1.000.030 max0.030 max0.15/0.350.40/0.650.40/0.700.15/0.30----
SNCM 415SNCM 220.12/0.180.40/0.700.030 max0.030 max0.15/0.350.40/0.651.60/2.000.15/0.30----
SNCM 420SNCM 230.17/0.230.40/0.700.030 max0.030 max0.15/0.350.40/0.651.60/2.000.15/0.30----
SNCM 431SNCM 10.27/0.350.60/0.900.030 max0.030 max0.15/0.350.60/1.001.60/2.000.15/0.30----
SNCM 439SNCM 80.36/0.430.60/0.900.030 max0.030 max0.15/0.350.60/1.001.60/2.000.15/0.30----
SNCM 447SNCM 90.44/0.500.60/0.900.030 max0.030 max0.15/0.350.60/1.001.60/2.000.15/0.30----
SNCM 616SNCM 260.13/0.200.80/1.200.030 max0.030 max0.15/0.351.40/1.802.80/3.200.40/0.60----
SNCM 625SNCM 20.20/0.300.35/0.600.030 max0.030 max0.15/0.351.00/1.503.00/3.500.15/0.30----
SNCM 630SNCM 50.25/0.350.35/0.600.030 max0.030 max0.15/0.352.50/3.502.50/3.500.50/0.70----
SNCM 815SNCM 250.12/0.180.30/0.600.030 max0.030 max0.15/0.350.70/1.004.00/4.500.15/0.30----
Remarks  1. As impurities Cu shall not exceed 0.30% throughout all classes
JIS G 4104 (1979) CHROMIUM STEELS
Symbol of classReference previous symbol%C%Mn%S%P%Si%Cr%Ni%Mo%V%B%W%Al
SCr 415SCr 210.13/0.180.60/0.850.030 max0.030 max0.15/0.35 0.90/1.20------
SCr 420SCr 220.18/0.230.60/0.850.030 max0.030 max0.15/0.35 0.90/1.20------
SCr 430SCr 20.28/0.330.60/0.850.030 max0.030 max0.15/0.35 0.90/1.20------
SCr 435SCr 30.33/0.380.60/0.850.030 max0.030 max0.15/0.35 0.90/1.20------
SCr 440SCr 40.38/0.430.60/0.850.030 max0.030 max0.15/0.35 0.90/1.20------
SCr 445SCr 50.43/0.480.60/0.850.030 max0.030 max0.15/0.35 0.90/1.20------
Remarks : As impurities Ni and Cu shall not exceed 0.25% and 0.30% respectively throughout all classes
JIS G 4105 (1979) CHROMIUM MOLYBDENUM STEELS
Symbol of classReference previous symbol%C%Mn%S%P%Si%Cr%Ni%Mo%V%B%W%Al
SCM 415SCM 210.13/0.180.60/0.850.030 max0.030 max0.15/0.35 0.90/1.20-0.15/0.30----
SCM 418-0.16/0.210.60/0.850.030 max0.030 max0.15/0.35 0.90/1.20-0.15/0.30----
SCM 420SCM 220.18/0.230.60/0.850.030 max0.030 max0.15/0.35 0.90/1.20-0.15/0.30----
SCM 421SCM 230.17/0.230.70/1.000.030 max0.030 max0.15/0.35 0.90/1.20-0.15/0.30 ---
SCM 430SCM 20.28/0.330.60/0.850.030 max0.030 max0.15/0.35 0.90/1.20-0.15/0.30--- 
SCM 432SCM 10.27/0.370.30/0.600.030 max0.030 max0.15/0.35 1.00/1.50-0.15/0.30--- 
SCM 435SCM 30.33/0.380.60/0.850.030 max0.030 max0.15/0.35 0.90/1.20-0.15/0.30----
SCM 440SCM 40.38/0.430.60/0.850.030 max0.030 max0.15/0.35 0.90/1.20-0.15/0.30----
SCM 445SCM 50.43/0.480.60/0.850.030 max0.030 max0.15/0.35 0.90/1.20-0.15/0.30----
SCM 822SCM 240.20/0.250.60/0.850.030 max0.030 max0.15/0.35 0.90/1.20-0.35/0.45----
Remarks : As impurities Ni and Cu shall not exceed 0.25% and 0.30% respectively throughout all classes
JIS G 4106 (1979) MANGANESE STEELS AND MANGANESE CHROMIUM STEELS FOR MACHINE STRUCTURAL USE
Symbol of classReference previous symbol%C%Mn%S%P%Si%Cr%Ni%Mo%V%B%W%Al
SMn 420SMn210.17/0.231.20/1.500.030 max0.030 max0.15/0.35 -------
SMn 433SMn 10.30/0.361.20/1.500.030 max0.030 max0.15/0.35 -------
SMn 438SMn 20.35/0.411.35/1.650.030 max0.030 max0.15/0.35 -------
SMn 443SMn 30.40/0.461.35/1.650.030 max0.030 max0.15/0.35 -------
SMnC 420SMnC210.17/0.231.20/1.500.030 max0.030 max0.15/0.35 0.35/0.70------
SMnC443SMnC 30.40/0.461.35/1.650.030 max0.030 max0.15/0.35 0.35/0.70------
Remarks : As impurities Ni and Cu shall not exceed 0.25% and 0.30% respectively throughout all classes SMn 420,SMn 433,SMn 438 and SMn 443 shall not contain Cr exceeding 0.35%
JIS G 4107 (1977) ALLOY STEEL BOLTING MATERIALS FOR HIGH TEMPERATURE SERVICE

Table 3 CHEMICAL COMPOSITION (LADLE ANALYSIS)

CLASSSYMBOL%C%Mn%S%P%Si%Cr%Ni%Mo%V%B%W%Al
Class 1SNB 50.10 min1.00 max0.030 max0.040 max1.00 max4.00/6.00-0.40/0.65----
Class 2SNB 70.38/0.480.75/1.000.040 max0.040 max0.20/0.350.80/1.10-0.15/0.25----
Class 3SNB 160.36/0.440.45/0.700.040 max0.040 max0.20/0.350.80/1.15-0.50/0.650.25/0.35---

Table 4 CHEMICAL COMPOSITION(PRODUCT ANALYSIS)

CLASSSYMBOL%C%Mn%S%P%Si%Cr%Ni%Mo%V%B%W%Al
Class 1SNB 50.090 min1.03 max0.035 max0.045 max1.05 max3.90/6.10-0.35/0.70----
Class 2SNB 70.36/0.500.71/1.040.045 max0.045 max0.18/0.370.75/1.15-0.13/0.27----
Class 3SNB 160.34/0.460.42/0.730.045 max0.045 max0.18/0.370.75/1.20-0.47/0.680.22/0.38---
JIS G 4108 (1977) ALLOY STEEL BARS FOR SPECIAL APPLICATION BOLTING MATERIALS

Table 2 CHEMICAL COMPOSITION (LADLE ANALYSIS)

CLASSSYMBOL%C%Mn%S%P%Si%Cr%Ni%Mo%V%B%W%Al
Class 1 Nos 1 to 5SNB21-1 to 50.36/0.440.45/0.700.025 max0.025 max0.20/0.350.80/1.15-0.50/0.650.25/0.35-- 
Class 2 Nos 1 to 5SNB22-1 to50.39/0.460.65/1.100.025 max0.025 max0.20/0.350.75/1.20-0.15/0.25----
Class 3 Nos 1 to 5SNB23-1 to 50.37/0.440.60/0.950.025 max0.025 max0.20/0.350.65/0.951.55/2.000.20/0.30----
Class 4 Nos 1 to 5SNB24-1 to 50.37/0.440.70/0.900.025 max0.025 max0.20/0.350.70/0.951.65/2.000.30/0.40----
JIS G 4108 (1977) ALLOY STEEL BARS FOR SPECIAL APPLICATION BOLTING MATERIALS

Table 3 CHEMICAL COMPOSITION (PRODUCT ANALYSIS)

CLASSSYMBOL%C%Mn%S%P%Si%Cr%Ni%Mo%V%B%W%Al
Class 1 Nos 1 to 5SNB21-1 to 50.34/0.460.42/0.730.030 max0.030 max0.18/0.370.75/1.20-0.47/0.680.22/0.38-- 
Class 2 Nos 1 to 5SNB22-1 to50.37/0.480.61/1.140.030 max0.030 max0.18/0.370.75/1.25-0.13/0.27----
Class 3 Nos 1 to 5SNB23-1 to 50.35/0.460.56/0.990.030 max0.030 max0.18/0.370.60/1.001.50/2.050.18/0.32----
Class 4 Nos 1 to 5SNB24-1 to 50.35/0.460.66/0.940.030 max0.030 max0.18/0.370.65/1.001.60/2.050.28/0.42----
JIS G 4202 (1979) ALUMINIUM CHROMIUM MOLYBDENUM STEELS

Table 2 CHEMICAL COMPOSITION (LADLE ANALYSIS)

CLASSSYMBOL%C%Mn%S%P%Si%Cr%Ni%Mo%V%B%W%Al
SACM 645SACM 10.40/0.500.60 max0.030 max0.030 max0.15/0.501.30/1.70-0.15/0.30---0.70/1.20
Remarks : As impurities Ni and Cu shall not exceed 0.25% and 0.30% respectively throughout all classes
JIS G 4303 (1981) STAINLESS STEEL BARS

Table 7 chemical composition for Austenitic Bars

Designation of grade%C%Mn%S%P%Si%Cr%Ni%Mo%V%B%W%Al
SUS 2010.15 max5.50/7.500.030 max0.060 max1.00 max16.00/18.003.50/5.50--0.25 max--
SUS 2020.15 max7.50/10.000.030 max0.060 max1.00 max17.00/19.004.00/6.00--0.25 max--
SUS 3010.15 max2.00 max0.030 max0.045 max1.00 max16.00/18.006.00/8.00-----
SUS 3020.15 max2.00 max0.030 max0.045 max1.00 max17.00/19.008.00/10.00-----
SUS 3030.15 max2.00 max0.15 min0.20 max1.00 max17.00/19.008.00/10.00-----
SUS 303Se0.15 max2.00 max0.060 max0.20 max1.00 max17.00/19.008.00/10.00-----
SUS 3040.080 max2.00 max0.030 max0.045 max1.00 max18.00/20.008.00/10.50-----
SUS 304L0.030 max2.00 max0.030 max0.045 max1.00 max18.00/20.009.00/13.00-----
SUS 304N10.080 max2.50 max0.030 max0.045 max1.00 max18.00/20.007.00/10.50--0.10/0.25--
SUS 304N20.080 max2.50 max0.030 max0.045 max1.00 max18.00/20.007.50/10.50--0.15/0.30--
SUS 304LN0.030 max2.00 max0.030 max0.045 max1.00 max17.00/19.008.50/11.50--0.12/0.22--
SUS 3050.12 max2.00 max0.030 max0.045 max1.00 max17.00/19.0010.50/13.00-----
SUS 309S0.080 max2.00 max0.030 max0.045 max1.00 max22.00/24.0012.00/15.00-----
SUS 310S0.080 max2.00 max0.030 max0.045 max1.00 max24.00/26.0019.00/22.00-----
SUS 3160.080 max2.00 max0.030 max0.045 max1.00 max16.00/18.0010.00/14.002.00/3.00----
SUS 316L0.030 max2.00 max0.030 max0.045 max1.00 max16.00/18.0012.00/15.002.00/3.00----
SUS 316N0.080 max2.00 max0.030 max0.045 max1.00 max16.00/18.0010.00/14.002.00/3.00-0.10/0.22--
SUS 316LN0.030 max2.00 max0.030 max0.045 max1.00 max16.50/18.5010.50/14.502.00/3.00-0.12/0.22--
SUS 316J10.080 max2.00 max0.030 max0.045 max1.00 max17.00/19.0010.00/14.001.20/2.751.00/2.50---
SUS 316JIL0.030 max2.00 max0.030 max0.045 max1.00 max17.00/19.0012.00/16.001.20/2.751.00/2.50---
SUS 3170.080 max2.00 max0.030 max0.045 max1.00 max18.00/20.0011.00/15.003.00/4.00----
SUS 317L0.030 max2.00 max0.030 max0.045 max1.00 max18.00/20.0011.00/15.003.00/4.00----
SUS 317J10.040 max2.50 max0.030 max0.045 max1.00 max16.00/19.0015.00/17.004.00/6.00----
SUS 3210.080 max2.00 max0.030 max0.045 max1.00 max17.00/19.009.00/13.00-----
SUS 3470.080 max2.00 max0.030 max0.045 max1.00 max17.00/19.009.00/13.00-----
SUS XM70.080 max2.00 max0.030 max0.045 max1.00 max17.00/19.008.50/10.50-3.00/4.00---
SUS XM15J10.080 max2.00 max0.030 max0.045 max3.00/5.0015.00/20.0011.50/15.00-----

Table 8 chemical composition for Austenitic Bars

Designation of grade%C%Mn%S%P%Si%Cr%Ni%Mo%V%B%W%Al
SUS 329 J10.080 max1.50 max0.030 max0.040 max1.00 max23.00/28.003.00/6.001.00/3.00----
Remarks- SUS XM 15J1 may be added alloying elements other than those in the above table as required  SUS303-0.60% or less of Mo may be added,SUS303 Se- Se- 0.15 minimum,SUS304N2- Nb- 0.15 max,SUS 347- Nb-10XC% min,SUS 321- Ti-5XC % min
JIS G 4303 (1981) STAINLESS STEEL BARS

Table 9 Chemical Composition for Ferritic Bars

Designation of grade%C%Mn%S%P%Si%Cr%Ni%Mo%CU%N%W%Al
SUS 4050.080  max1.00 max0.030 max0.040 max1.00 max11.50/14.50-----0.10/0.30
SUS 410L0.030 max1.00 max0.030 max0.040 max1.00 max11.00/13.50------
SUS 4300.12 max1.00 max0.030 max0.040 max0.75 max16.00/18.00------
SUS 430F0.12 max1.25 max0.15 min0.060 max1.00 max16.00/18.00------
SUS 4340.12 max1.00 max0.030 max0.040 max1.00 max16.00/18.00-0.75/1.25----
SUS 447J10.010 max0.40 max0.020 max0.030 max0.40 max28.50/32.00-1.50/2.50-0.015 max--
SUS XM270.010 max0.40 max0.020 max0.030 max0.40 max25.00/27.50-0.75/1.50-0.015 max--
Note: SUS 430F-0.60% or less of Mo may be added Each grade other than SUS 447 J1 and SUS XM27 may contain 0.60% or less of Ni SUS447J1 and SUS XM @& may contain 0.50% or less of Ni, 0.20% or less of Cu and 0.50% or less of Ni + Cu and as required may be added alloying elements other than those in the above table

Table 10 Chemical Composition for Martensitic Bars

Designation of grade%C%Mn%S%P%Si%Cr%Ni%Mo%V%N%W%Al
SUS 4030.15 max1.00 max0.030 max0.040 max0.50 max11.50/13.00-3-----
SUS 4100.15 max1.00 max0.030 max0.040 max1.00 max11.50/13.50-3-----
SUS 410J10.080/0.181.00 max0.030 max0.040 max0.60 max11.50/14.00-30.30/0.60----
SUS 4160.15 max1.25 max0.15 min0.060 max1.00 max12.00/14.00-3-4----
SUS420J10.16/0.251.00 max0.030 max0.040 max1.00 max12.00/14.00-3-----
SUS 420J20.26/0.401.00 max0.030 max0.040 max1.00 max12.00/14.00-3-----
SUS 420F0.26/0.401.25 max0.15 min0.060 max1.00 max12.00/14.00-3-4----
SUS 4310.20 max1.00 max0.030 max0.040 max1.00 max15.00/17.001.25/2.50-----
SUS 440A0.60/0.751.00 max0.030 max0.040 max1.00 max16.00/18.00-3-5----
SUS 440B0.75/0.951.00 max0.030 max0.040 max1.00 max16.00/18.00-3-5----
SUS440C0.95/1.201.00 max0.030 max0.040 max1.00 max16.00/18.00-3-5----
SUS440F0.95/1.201.25 max0.15 min0.060 max1.00 max16.00/18.00-3-5----
Note:-3-- 0.60% or less of Ni may be added,-4-- 0.60% or less of Mo may be added,-5-- 0.75% or less of Mo may be added

Table 11 Chemical Composition for Precipitation hardening Bars

Designation of grade%C%Mn%S%P%Si%Cr%Ni%Mo%CU%B%W%Al
SUS 6300.070 max1.00 max0.030 max0.040 max1.00 max15.50/17.503.00/5.00-3.00/5.00Nb- 0.15/0.45--
SUS 6310.090 max1.00 max0.030 max0.040 max1.00 max16.00/18.006.50/7.75----0.75/1.50
JIS G 4311 (1981) HEAT - RESISTING STEEL BARS

Table 5 Chemical Composition for Austenitic Bars

Designation of grade%C%Mn%S%P%Si%Cr%Ni%Mo%N%B%W%Al%Co
SUH 310.35/0.450.60 max0.030 max0.040 max1.50/2.5014.00/16.0013.00/15.00---2.00/3.00--
SUH 350.48/0.588.00/10.000.030 max0.040 max0.35 max20.00/22.003.25/4.50--0.35/0.50---
SUH 360.48/0.588.00/10.000.040/0.0900.040 max0.35 max20.00/22.003.25/4.50--0.35/0.50---
SUH 370.15/0.251.00/1.600.030 max0.040 max1.00 max20.50/22.5010.00/12.00--0.15/0.30---
SUH 380.25/0.351.20 max0.030 max0.18/0.251.00 max19.00/21.0010.00/12.001.80/2.50-----
SUH 3090.20 max2.00 max0.030 max0.040 max1.00 max22.00/24.0012.00/15.00------
SUH 3100.25 max2.00 max0.030 max0.040 max1.50 max24.00/26.0019.00/22.00------
SUH 3300.15 max2.00 max0.030 max0.040 max1.50 max14.00/17.0033.00/37.00------
SUH 6600.080 max2.00 max0.030 max0.040 max1.00 max13.50/16.0024.00/27.001.00/1.500.10/0.50--0.35 max-
SUH 6610.080/0.161.00/2.000.030 max0.040 max1.00 max20.00/22.5019.00/21.002.50/3.50-0.10/0.202.00/3.00-18.50/21.00
Remarks: Other Elements in given below grade SUH 38- Boron- 0.001/0.010, SUH- 660- Ti- 1.90/2.35% and  Boron-0.001/0.010 SUH 661- Nb- 0.75/1.25% 

Table 6 Chemical Composition for Ferritic Bars

Designation of grade%C%Mn%S%P%Si%Cr%Ni%Mo%N%B%W%Al%Co
SUH 4460.20 max1.50 max0.030 max0.040 max1.00 max23.00/27.00---0.25 max---
Remarks: 0.30% or less of Cu may be contained 0.60% or less of Ni may be contained

Table 7 Chemical Composition for Martensitic Bars

Designation of grade%C%Mn%S%P%Si%Cr%Ni%Mo%V%B%W%Al%Co
SUH 10.40/0.500.60 max0.030 max0.030 max3.00/3.507.50/9.501------
SUH 30.35/0.450.60 max0.030 max0.030 max1.80/2.5010.00/12.0010.70/1.30-----
SUH 40.75/0.850.20/0.600.030 max0.030 max1.75/2.2519.00/20.501.15/1.65------
SUH 110.45/0.550.60 max0.030 max0.030 max1.00/2.007.50/9.501------
SUH 6000.15/0.200.50/1.000.030 max0.040 max0.50 max10.00/13.0010.30/0.900.10/0.400.050/0.10Nb- 0.20/0.60-
SUH 6160.20/0.250.50/1.000.030 max0.040 max0.50 max11.00/13.000.50/1.000.75/1.250.20/0.30-0.75/1.25--
Remarks: 1 in Nickel column  represent 0.60% or less of Ni may be contained 0.30% or less of Cu may be contained
JIS G 4801 (1984) SPRING STEELS
Designation of grade%C%Mn%S%P%Si%Cr%Ni%Mo%V%B%W%Al%Co
SUP30.75/0.900.30/0.600.035 max0.035 max0.15/0.35--------
SUP60.56/0.640.70/1.000.035 max0.035 max1.50/1.80--------
SUP70.56/0.640.70/1.000.035 max0.035 max1.80/2.20--------
SUP90.52/0.600.65/0.950.035 max0.035 max0.15/0.350.65/0.95-------
SUP9A0.56/0.640.70/1.000.035 max0.035 max0.15/0.350.70/1.00-------
SUP100.47/0.550.65/0.950.035 max0.035 max0.15/0.350.80/1.00--0.15/0.25----
SUP11A0.56/0.640.70/1.000.035 max0.035 max0.15/0.350.70/1.00---0.0005 min---
SUP120.51/0.590.60/0.900.035 max0.035 max1.20/1.600.60/0.90-------
SUP130.56/0.640.70/1.000.035 max0.035 max0.15/0.350.70/0.90-0.25/0.35-----
Remarks: As impurities Cu content for each grade shall not exceed 0.30%
JIS G 4804 (1983) RESULPHYRIZED CARBON STEELS
Designation of grade%C%Mn%S%P%Si%Cr%Ni%Mo%V%Pb%W%B%Co%Al
SUM 110.080/0.130.30/0.600.080/0.130.040 maxRefer note---------
SUM 120.080/0.130.60/0.900.080/0.130.040 maxRefer note---------
SUM 210.13 max0.70/1.000.16/0.230.070/0.12Refer note---------
SUM 220.13 max0.70/1.000.24/0.330.070/0.12Refer note---------
SUM 22L0.13 max0.70/1.000.24/0.330.070/0.12Refer note----0.10/0.35----
SUM 230.090 max0.75/1.050.26/0.350.040/0.090Refer note---------
SUM 23L0.090 max0.75/1.050.26/0.350.040/0.090Refer note----0.10/0.35----
SUM 24L0.15 max0.85/1.150.26/0.350.040/0.090Refer note----0.10/0.35----
SUM 250.15 max0.50/1.400.30/0.400.070/0.12Refer note---------
SUM 310.14/0.201.00/1.300.080/0.130.040 maxRefer note---------
SUM 31L0.14/0.201.00/1.300.080/0.130.040 maxRefer note----0.10/0.35----
SUM 320.12/0.200.60/1.100.10/0.200.040 maxRefer note---------
SUM 410.32/0.391.35/1.650.080/0.130.040 maxRefer note---------
SUM 420.37/0.451.35/1.650.080/0.130.040 maxRefer note---------
SUM 430.40/0.481.35/1.650.24/0.330.040 maxRefer note---------
Note : 1. As to silicon no requirement shall be provided as a rule. If the need arises, such range or limiting values as 0.10% and under 0.10 to 0.20% or 0.15 to 0.35% may be selected to be used by agreement between the manufacturer and purchaser. 2. When lead content is reported it shall be expressed by the range of 0.10 to 0.35 %
JIS G 4805 (1970) HIGH CARBON CHROMIUM BEARING STEELS
Symbol%C%Mn%S%P%Si%Cr%Ni%Mo%V%Pb%W%B%Co%Al
SUJ 10.95/1.100.50 max0.025 max0.025 max0.15/0.350.90/1.20--------
SUJ 20.95/1.100.50 max0.025 max0.025 max0.15/0.351.30/1.60--------
SUJ 30.95/1.100.90/1.150.025 max0.025 max0.40/0.700.90/1.20--------
SUJ 40.95/1.100.50 max0.025 max0.025 max0.15/0.351.30/1.60-0.10/0.25------
SUJ 50.95/1.100.90/1.150.025 max0.025 max0.40/0.700.90/1.20-0.10/0.25------
               
Note : 1. The steels shall not contain more than 0.25% of Ni and Cu respectively as impurites except that Cu in wire steel shall not exceed 0.20% SUJ 1, SUJ 2 and SUJ 3 shall not contain more than 0.080 % of Mo 2. Not more than 0.25% of elements other than those specified in Table 2 may be added 3.When steel worked in the acid furnaces the steels may contain P and S up to 0.030% respectively and SUJ 1,SUJ 2,and SUJ 4 may contain Si up to 0.40%